COC TOPAS 6013M-07 产品说明:
Product Description
TOPAS 6013M-07 is an injection molding grade with a wide processing window, especially suited for blow molding processes including IBM and ISBM. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve content stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (130°C) heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures.
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.02 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率) (260°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (260°C/2.16 kg) | 13.0 | cm3/10min | ISO 1133 |
收缩率 1 | 0.50 到 0.70 | % | 内部方法 |
吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 2900 | MPa | ISO 527-2/1A/1 |
拉伸应力 (屈服) | 63.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 (屈服) | 2.6 | % | ISO 527-2/1A/50 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 (23°C) | 2.0 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度 (23°C) | 14 | kJ/m2 | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 (0.45 MPa, 未退火) | 130 | °C | ISO 75-2/B |
玻璃转化温度 | 142 | °C | ISO 11357-2 |
COC特性:
环烯烃共聚物 是一种无定形高分子聚合物制造商生产的几个。 COC是一类新的聚合物相对较 聚丙烯 和 聚乙烯。这种材料主要用于要求玻璃般清晰包括镜头,瓶,显示器和医疗
设备的应用程序。COCs良好的耐化学性。
挤压 COC既可以挤压铸造和吹膜设备。主要用于消费应用,包括食品和药品包装。
成型 COC是主要用于注射成型。
TOPAS是宝理公司开发出来的环烯烃类共聚物(COC)的商品名,是具有环状烯烃结构的非晶性透明共聚高分子。
TOPAS 具有与PMMA(聚甲基丙烯酸甲酯、丙烯酸树脂)相匹敌的光学性能以及具有高于PC(聚碳酸酯)的耐热性,还具有比PMMA和PC更加优良的尺寸稳定性等,在市场上获得了很
高的评价。再有,TOPAS 还具有改善水蒸汽气密性,增加刚性、耐热性,易赋予切割性能等优点,作为适合于用作传统材料的改性用材料,它在包装材料领域里的开发活动正在推进之中。是玻璃材料的最佳替代材料。